Strong acid and alkali resistant vinyl ester flooring-Guangdong Jinfeng New Material Technology Co., Ltd

Productproduct category

National Service Hotline

15015150026

Your location：Home->Product->Anti-Corrosion Flooring Series

Strong acid and alkali resistant vinyl ester flooring

[View the original image] [return]

[The previous one:Anti corrosion pool project] [Next:最后一篇]

Strong acid and alkali resistant vinyl ester flooring

Details

Thickness

1.0mm 2.0mm 3.0mm

Surface Finish

Self-leveling trowel finish, roller finish, glossy finish

Service Life

More than 10 years

Floor Performance

Flat and seamless surface, dust-free and easy to clean; it features sound mechanical strength and excellent chemical resistance, capable of resisting high-concentration sulfuric acid.

Scope of Application

① Chemical plants, electroplating factories, battery factories, sewage treatment plants and other facilities;

② Sites with stringent requirements for anti-corrosion performance.

Construction Process

①Waterproofing Treatment

The ground floor shall be completed with waterproofing works in advance.

②Base Surface Treatment

Repair, grind and remove dust according to the actual condition of the substrate.

③Epoxy Primer

Roll apply 1 to 2 coats of epoxy primer with excellent permeability and adhesion to improve substrate strength and bonding force.

④Special Anti-corrosion Primer

Roll one coat of sealing special anti-corrosion primer with strong adhesion to enhance the bonding between the base surface and fiberglass cloth.

⑤Fiberglass Cloth Laying

Lay fiberglass cloth flat on the floor, bond it with mixed special anti-corrosion intermediate coating, then level evenly with a putty knife for uniform coverage. Lay 1 to 3 layers as required to improve floor toughness.

⑥Special Anti-corrosion Intermediate Coat

Mix special epoxy intermediate coat with appropriate quartz sand, then evenly apply 1 to 3 coats with a trowel.

⑦Special Anti-corrosion Putty

Apply 2 to 3 coats as required until the surface is flat and pore-free to facilitate topcoat construction.

⑧Special Anti-corrosion Color Coat

Roll two coats of special anti-corrosion color paint to achieve uniform color.

⑨Special Anti-corrosion Topcoat

Trowel one coat of special anti-corrosion self-leveling topcoat, or roll two coats of special anti-corrosion clear topcoat. The finished floor is bright, clean and uniform in color.

⑩Completion & Curing

Pedestrian access is allowed after 24 hours; heavy load access after 72 hours. The floor can be officially put into use after 7 days of curing. (Based on 25℃; opening time shall be properly extended at low temperature. Keep the floor free of water during the curing period.)

Technical Specifications

Item	Index
Surface Drying Time (h)	≤4
Hard Drying Time (h)	≤24
Hardness (Shore Hardness Type D)	≥80
Wear Resistance (750g/500r, Weight Loss, g)	≤0.03
Wear Resistance (750g/500r, Weight Loss, g)	≥80
Tensile Strength (MPa)	≥100
Bonding Strength (MPa)	≥3

Chemical Resistance Performance：

Chemical Name	Performance	Chemical Name	Performance
10% Sulfuric Acid	No change within 24 days	Toluene	No change within 24 days
60% Sulfuric Acid	No change within 24 days	Xylene	No change within 24 days
98% Sulfuric Acid	No change in 31h; surface roughened in 10 days	95% Ethanol	Softened in 16h; surface roughened in 14 days
37% Hydrochloric Acid	No change in 14 days; discolored in 24 days	Butanol	No change in 31h; softened in 10 days
Phosphoric Acid	No change in 14 days; surface roughened in 24 days	Ethylene Glycol	No change within 24 days
10% Nitric Acid	No change within 24 days	Butyl Ester	No change in 16h; softened in 10 days
10% Formic Acid	Softened in 16h; stable in 14 days	37% Formaldehyde	No change within 24 days
5% Acetic Acid	No change within 24 days	Hydrogen Peroxide	No change within 24 days
10% Acetic Acid	No change in 16h, softened in 31h, stable in 24 days	Cyclohexane	No change within 24 days